Redoflex

Redoflex
Product Description

Redoflex GG

TWO COMPONENT GUN GRADE POLYSULPHIDE SEALANT


DESCRIPTION

Redoflex GG is a cross linking polysulphide based elastic sealant for vertical and horizontal expan- sion joints. Suitable for use in hot and tropical climatic conditions.


USES

It is used in both vertical and horizontal expansion joints in many types of buildings and civil engineering constructions such as:

Retaining walls

Underpasses and tunnels

Reservoirs

Precast concrete elements

Bridges

High and low rise buildings and

Wherever a permanently flexible seal is required


CHARACTERISTICS / ADVANTAGES

Easy to use

Economical

Excellent adhesion with many materials

Non- sag in vertical and overhead joints

Good chemical resistance

Permanently elastic

Good weather resistance


SUSTAINABILITY

VOC content <35 g/L (less water) US EPA 24


APPROVALS / CERTIFICATES

Conforms to: BS 4254 - 1983

Conforms to BS 6920:1998 (Gun Grad grey)

Complies with ASTM C920, Type M, Grade NS, Class 25

Conforms to: TT-S00227 E (COM-NBS) - 3 Type ll


PRODUCT INFORMATION

Chemical base : Cross linking polysulphide

Packaging : 4 kg (Comp. A + Comp. B),  8 kg (Comp. A + Comp. B)

Colour : Paste, grey

Shelf life :Redoflex GG has a shelf life of 12 months from the date of production, if it is stored in undamaged, original, sealed packaging, and if the storage conditions are met.

Storage conditions :  Redoflex GG shall be stored in dry conditions, where it is protect-

ted from direct sunlight and at temperatures between 5oC and 30oC.

Density :  ~1.75gm/cc

Solid content : 100 %


TECHNICAL INFORMATION

Shore A Hardness : 20 to 25 (ASTM C 661)

Movement Capability : +/-25 % (ASTM C 719)

Service Temperature : -20oC min. / +80oC max.

Joint Design : Joint Configuration Minimum joint width: 6 mm Maximum Joint width: 50 mm

Redoflex GG may be applied to joints between 5 and 50 mm wide. Joints which are expected to experience cyclic movements should be designed to an optimum width: depth ratio of 2:1, subject to the overriding recommended minimum sealant depths set out below: 5 mm for metals, glass and other non-porous surfaces; 10 mm for all porous surfaces; 20 mm for trafficked joints and those subject to hydrostatic pressures.

At chamfered elements it shall not fill the chamfer with sealant.


Mixing Ratio : Part A : Part B = 3 : 1 (by weight)

Ambient Air Temperature : +5oC min. / +50oC max.

Substrate Temperature : +5 oC min. / +50oC max.

Substrate Moisture Content : Dry joint with sound concrete edges. For joints under wet conditions, use Primer US60

Pot Life : 2 h at 25oC

Curing Time : 4 weeks at 5oC, 2 weeks at 15oC, 1 week at 25oC


APPLICATION INSTRUCTIONS

SUBSTRATE PREPARATION

All surfaces must be clean, dry and free from any loosely adhering particles.

Check the joints edges for soundness and if found weak cut recess and fill up with suitable repair mortar (Consult Redoflex Technical Department). Correct joint depth can be established by inserting closed cell poly- ethylene backing rod tightly into the joint. When the joints have been filled with fiber filled board, this must be raked back to the required depth. Use bond break- ertape over the backer material. Protect surfaces with masking tape.


PRIMING

Non-porous surfaces

Use Primer US60 on glass, ceramics and metals. The one part chemically active clear liquid is to be applied by brush or pad. One thin coat should be applied and allowed to dry for 2 to 5 minutes prior to sealant application


Porous surfaces

Primer US60: It is a high performance chemically active non-toxic liquid for brush application to prime all concrete, stone, brickwork, timber and unglazed edges of ceramic tiles. Apply one thin coat using a clean, dry brush, ensuring complete coverage. Avoid over priming resulting in an excess of primer in the base of the joint or application beyond faces. The mixed Redoflex GG must be applied when the primer is tack free, that is after the evaporation of the solvent but before the primer film has completely reacted. After 6 hours @ 20oC, or 3 hours @ 35oC the surfaces must be re- primed before applying the sealant.


APPLICATION METHOD / TOOLS

Where required, protect the surface with masking tape. To place, load the mixed sealant directly into bulk or caulking gun or using a follower plate loading system. Install the sealant into the joint without trap- ping air with consistent pressure to force the sealant into the joint. Tool-off with a spatula to form slightly concave profile. Remove masking tape.


CLEANING OF TOOLS

Clean all tools and application equipment with Redwop Sol2 Cleaner immediately after use. Hardened / cured material can only be mechanically removed.

The product is packed in a 4 kg tin, containing the base and curing agent, ready to mix in the appropriate ratios. Mix the product thoroughly with a mixing paddle fitted to an electric hand drill not exceeding 500 rpm to avoid entrapping air. Mix for approximate- 5 mixing minutes until a smooth, even consistency is achieved.


LIMITATIONS

Do not use in contact with drinking water or food.

Gun grade Redoflex GG is gun-applied 2 part polysulphide sealant which is used both for hori- zontal and vertical joints. Sealant joint movement should not exceed +/-25 % of the joint width when installed in a width to depth ratio of 2 : 1.

Redoflex GG is chemical resistant (occa- sional spillages) to diluted acids, diluted alkalis, avi- ation fuel, kerosene, lubrification oils, skydrol and white spirit.

Redoflex GG is not chemical resistant to chlorinated solvents, aromatic solvent and diluted oxidizing acids.

Redoflex GG must be fully cured before permanent immersion in water.

Paint compatibility with sealant should be checked prior to painting.


BASIS OF PRODUCT DATA

All technical data stated in this Data Sheet are based on laboratory tests. Actual measured data may vary due to circumstances beyond our control.


Storage

Redoflex GG and Primer US60 have a storage life of 12 months kept in original containers and stored in dry conditions between 5oC and 27oC.


LEGAL NOTES

The information, and, in particular, the recommendations relating to the application and end-use of Redoflex products, are given in good faith based on Redoflex's cur- rent knowledge and experience of the products when properly stored, handled and applied under normal conditions in accordance with Redoflex's recommendations. In practice, the differences in materials, subtracts and actual site conditions are such that no war- ranty in respect of merchantability or of fitness for a particular purpose, nor any liability arising out of any legal relationship whatsoever, can be inferred either from this information, or from any written recommendations, or from any other advice offered. The user of the product must test the products suitability for the intended application and purpose. Redoflex re-serves the right to change the properties of its products. The proprietary rights of third parties must be observed. All orders are accepted subject to our current terms of sale and delivery. Users must always refer to the most recent issue of the local Product Data Sheet for the product concerned, copies of which will be supplied on request.


Precautions Health and safety

Redoflex GG and Primer US60 should not come in contact with skin and eyes or be swallowed. Avoid breathing of vapor. Splashes must be washed off immediately. Wear impervious rubber or PVC gloves and eye protection. Hands should be thoroughly washed with soap and water before eating or smoking. In the case of eye contact seek medical attention immediately.

Redoflex GG curing agent consists of a heavy metal based oxide. Cured sealant should not be burned off due to the generation of toxic fumes. Empty containers must be collected for careful disposal and not left lying.